Typical Tensile Properties
| PWHT 620°C 1h | |||
| Elongation | Tensile Strength | Yield Strength | 保护气体 |
| 27 % | 560 MPa | 460 MPa | ISO |
| - | - | - | AWS |
夏比V型缺口冲击性能
| PWHT 620°C 1h | ||
| Impact Value | Testing Temperature | 保护气体 |
| 175 J | 20 °C | ISO |
焊缝金属分析
| Mn | ||||
| Mn | Mo | C | Si | Cr |
| 0.77 % | - | - | - | - |
| Mo | ||||
| Mn | Mo | C | Si | Cr |
| - | 0.57 % | - | - | - |
| C | ||||
| Mn | Mo | C | Si | Cr |
| - | - | 0.05 % | - | - |
| Si | ||||
| Mn | Mo | C | Si | Cr |
| - | - | - | 0.38 % | - |
| Cr | ||||
| Mn | Mo | C | Si | Cr |
| - | - | - | - | 0.04 % |
熔敷数据
| Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
| 40 sec | 0.59 kg | 136.0 | 55-80 A | 0.7 kg/h | 22 V | 2.0 x 300 mm |
| 55 sec | 0.59 kg | 73.0 | 75-110 A | 0.9 kg/h | 23 V | 2.5 x 350 mm |
| 66 sec | 0.54 kg | 53 | 105-150 A | 1 kg/h | 23 V | 3.2 x 350 mm |
| 81 sec | 0.59 kg | 37.0 | 105-150 A | 1.2 kg/h | 25 V | 3.2 x 450 mm |
| 90 sec | 0.65 kg | 22.5 | 140-200 A | 1.8 kg/h | 26 V | 4.0 x 450 mm |
| 104 sec | 0.65 kg | 14.5 | 190-270 A | 2.4 kg/h | 27 V |
5.0 x 450 mm |